Improving Performance of Stamping Dies with Ion/Plasma Nitriding

This article originally appeared in Industrial Heating, November 2015. Scroll below to learn more about improving stamping dies with ion/plasma nitriding.

posted On Thursday, August 8, 2019 in Blog

This article was written by AHT employees, Edward Rolinski, Mike Woods and Gary Sharp. It originally appeared on Industrial Heating's website. The below has been shortened from the original article. See the full version here.

The strength of steels has significantly exceeded what was used in older designs. Some of the automotive components, such as floor panels, are even made of press-hardened steels (PHS) with tensile strength reaching 1,500-1,800 MPa.[1] Therefore, challenges for stamping tools used in those applications are very high. Ion/plasma nitriding is a technique that has been very successful in surface hardening those tools in recent years.[2-7] This is especially true when the dies are made of cast materials alloyed with chromium, molybdenum and other elements that form very stable and hard nitrides. Nitrided layers formed in those alloys are very hard, and their depth exceeds 0.25 mm (0.010 inch).

Chromium Plating Limitations

Chromium plating has been historically used for stamping dies. It offers a very smooth surface with a low coefficient of friction, although not as low as ion-nitrided cast materials.[2] Limitations of chromium plating seem to be strained as higher-strength steels become harder than the substrate below the surface of the chromium layer.

(RELATED BLOG: Why You Should Protect Your Parts with Compound Zone instead of Coatings)

With the ever-increasing hardness of panel materials, the surface requires more protection than just a chromium layer of 10-20 micrometers. Also, the electrolytic process of depositing chromium means that the chromium deposit will be heavier on most protruding areas and will be very thin and possibly nonexistent on recessed areas, possibly resulting in dimensional differences.

In contrast, nitriding is not a coating, so it does not chip or peel. It will provide the substrate depth hardness required to withstand a greater-impact environment, which results in less slug damage.[4-8] It also does not cause dimensional changes since the process is evenly applied on both protruding and recessed areas.

Previous surveys have shown that a chromium-plated die surface on cast iron or cast steel can see as many as 350,000-600,000 hits or panels. These numbers are decreasing because of the wider applications of advanced high-strength steels (AHSS). In the same stamping environment, however, nitriding results show quality panels well in excess of 850,000 hits with dies that are still running. One particular study showed 1.2 million panels on a floor-pan die cavity.

Ion/Plasma Nitriding Best Treatment for Stamping Dies

The process has been widely used for hardening components of large-draw dies such as punches and binders.[3-7] They are typically made of gray or ductile cast irons (such as G2500, G3500, D5506 and others) as well as cast steels, including S0050A and D-2. The line and progressive dies as well as various inserts are made of Caldie, M-2, S-7 and other high-quality tool steels and are often treated in a combination of ion/plasma nitriding with PVD coatings.[9]

The best option for treating monolithic, large-size die components is ion/plasma nitriding. The treatment is performed in a large vacuum vessel equipped with resistance heaters and a plasma generator. Parts are covered with glow-discharge plasma, which generates ions and active nitrogen species and causes nitriding effect. 

The nitrided layer is built of compound and diffusion layers. It can be very easily noted that the hardness profile in the ion/plasma-nitrided sample is more advantageous than in the chromium-plated sample. A very sharp gradient of hardness in the latter may be a reason for cracking and exfoliation of the chromium layer in the high-stress contact areas such as radii. Conversely, a smooth transition of hardness in the surface of the ion/plasma-nitrided dies is preferable for all metal-forming tools subjected to very high Hertzian stresses. It should also be noted that the stresses in nitrided surfaces are compressive.[10]


New generations of advanced high-strength steels (AHSS) used in the auto industry create challenging situations for stamping tools since the stress required to induce sufficient plastic deformation exceeds 400 MPa. Small tools or inserts can be made of the strongest tool steels, nitrided and PVD or CVD coated with hard and wear-resistant layers such as CrN, TiAlN, etc. to endure to the contact stresses needed for forming the steel components.

Large stamping tools are usually made of cast irons or cast steels. Hardness of such materials is typically insufficient for resisting high-contact Hertzian stresses needed in the forming operations. These tools can be induction or flame hardened, but treatments with PVC or PVD techniques are not accessible to them because of their size. Chromium plating has been used successfully in those situations for many years, but this technique has reached its limits for tools needed in forming AHSS.

Ion nitriding can produce hard surface layers in any ferrous or titanium alloy components. The nitrided layer produced in high-alloy precipitation-hardenable steels (such as 15-5 PH, 17-4 PH or others) is free of the intergranular network (IGN) and has a white layer of limited thickness, making the components resistant to wear, bending fatigue and rolling-contact fatigue (RCF).

Questions about Ion/Plasma Nitriding and Stamping Dies? Fill out our Contact Form

AHT has locations in Iowa, Alabama and Michigan. View the locations and contact information here: https://www.ahtcorp.com/locations/


1. Billur E. and Altan T. “Three generations of advanced high-strength steels for automotive applications, Part I,” Stamping Journal, November/December, 2013, pp. 16-17

2. Meuleman D. J. and Dwyer T. E. “Die Materials and Treatment with Electrogalvanized Steels,” SAE Technical Paper Series, 880369, 1988, pp. 51-60

3. Roliński E., Damirgi T., and Sharp G., “Plasma and Gas Nitriding for Engineering Components and Metal Forming Tools,” Industrial Heating, May 2012, pp. 53-56

4. Roliński E., Konieczny A., Sharp G., “Nature of Surface Changes in Stamping Tools of Gray and Ductile Cast Iron During Gas and Plasma Nitrocarburizing,” Journal of Materials Engineering and Performance, 2009, Vol. 18, No 8, pp. 1052-1059

5. Roliński E., Konieczny A., Sharp G., “Influence of Nitriding Mechanisms on Surface Roughness of Plasma and Gas Nitrided/Nitrocarburized Gray Cast Iron,” Heat Treating Progress, March/April 2007, pp. 39-46

6. Roliński E., Konieczny A., Sharp G., “Plasma Nitriding Automotive Stamping Dies,” Heat Treating Progress, September/October 2006, Vol. 6, No 5, pp. 19-23

7. Roliński E., and Sharp G., “When and Why Ion Nitriding/Nitrocarburizing Makes Good Sense,” Industrial Heating, Aug. 2005, pp. 67-72

8. NASF Report, “EPA Issues Chromium Air Rule, Despite NASF Meeting With White House Officials,” Product Finishing, Sep. 2012, p. 10

9. Madorsky Y., Thompson M., “Coatings for stamping and forming tools,” Stamping Journal, March 2005, pp. 30-34

10.  E. Roliński, ”Plasma Assisted Nitriding and Nitrocarburizing of Steel and other Ferrous Alloys,” Chapter 11 in reference 11, pp. 413-457

11.  E. J. Mittemeijer and M. A. J. Somers Ed, Thermochemical Surface Engineering of Steels, 2014 Woodhead Publishing Series in Metals and Surface Engineering: Number 62, Cambridge, CB22, 3HJ, UK, Waltham, MA, U.S.A. Kidlington, OX5 1GB, UK pp. 1-792

12.  M. Rhodes, M. Johnson, K. Miedema, J. Scheetz and J. Williams, Introduction of Nitrided M50 and M50NiL Bearings Into Jet Engine Mainshaft Applications, BEARING STEEL TECHNOLOGIES: 10TH VOLUME, ADVANCES IN STEEL TECHNOLOGIES FOR ROLLING BEARINGS, STP 1580, 2015, pp. 259-271

  1. automotive
  2. cast iron
  3. ion nitriding
  4. nitriding
  5. plasma nitriding
  6. stamping dies